Factory Direct white paint talc powder 5000 mesh Average particle diameter 2-3um Superfine(Raw Powder)

日期:2013/9/17 17:54:48 人气:3898

Product Data Sheet                                       Superfine(Raw Powder)

 

This product is a highly pure white talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, good dispersity, more platy, excellent improved stiffness/impact balance of products, unique performance, low shrinkage rate, excellent scratch resistance property, it is suitable for reinforcement of high-end polymers and nucleant in semi-crystalline polymers.

 

Uncompacted form  

Loose bulk density :                          M.I. 93003                                       0.11 g/cm3

Moisture content at 105 °C :            ISO 787/2 - M.I. 93005                  0.2%

 

Brightness by Minolta CR300 

Y                                                               96.0

L*   (CIE)                                                 98.5

a*   (CIE)                                                 0.2

b*   (CIE)                                                 0.5

 

Particle Size Distribution by Sedigraph                                                  by Laser Mastersizer 

Sedimentation analysis ,                                                                              Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                         Mie Theory  (ISO 13320-1)

Median Diameter-D50:0.75(1.0)*µm D95:2.5µm                                    MedianDiameter-D50:3.5(5)*µm D95: 7.0µm

Particle Size Distribution.png

Physical Properties  

Density                                        DIN 53193                  2.8 g/cm3

Specific Surface B.E.T.            DIN 66131/2                11 m2/g

Hardness                                  Mohs scale                   1

 

Chemical Analyses  

SiO2                                                           61.5%

MgO                                                           31.5%

CaO                                                           0.2%

Fe2O3                                                       0.2%

Al2O3                                                        0.2%

Loss on Ignition at 1050°C                  6.0%