Odorless white talc powder for industrial use plastic filler T Series 1500 meshes(Raw White)

日期:2016/9/14 10:21:17 人气:2745

Product Data Sheet                                        T Series 1500 meshes(Raw White)

This product is a highly pure white talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, good dispersity, more platy, excellent improved stiffness/impact balance of products, unique performance, low shrinkage rate, stable dimension, it is suitable for reinforcement of polymers, it is recommended for polypropylene automotive exterior parts, interior parts, bumpers and dashboard products of high-end auto.

 

Uncompacted form  

Loose bulk density :                         M.I. 93003                                      0.20 g/cm3

Moisture content at 105 °C :           ISO 787/2 - M.I. 93005                 0.2%

 

Brightness by Minolta CR300 

Y                                                               92.0

L*   (CIE)                                                 95.2

a*   (CIE)                                                  0.2

b*   (CIE)                                                  0.5

 

Particle Size Distribution by Sedigraph                                                  by Laser Mastersizer 

Sedimentation analysis ,                                                                             Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                        Mie Theory  (ISO 13320-1)

Median Diameter -D50: 3.0 (3)*µm  D95: 6.8µm                                    Median Diameter - D50: 6.5 (8)*µm   D95: 14.9µm

Particle Size Distribution.png

 

Physical Properties  

Density                                                    DIN 53193                         2.8 g/cm3

Specific Surface B.E.T.                         DIN 66131/2                      6 m2/g

Hardness                                                 Mohs scale                        1

 

Chemical Analyses  

SiO2                                                          58.0%

MgO                                                           31.5%

CaO                                                           0.2%

Fe2O3                                                       0.2%

Al2O3                                                         0.2%

Loss on Ignition at 1050°C                    8.9%