Highly pure grey modified polymers Hydrous magnesium silicate W Series 1250 meshes(dark color)

日期:2013/9/17 17:52:58 人气:3927

Product data sheet                                       W Series 1250 meshes(dark color)

This product is a highly pure grey talc, and it is a special talc for grey modified polymers. Due to its uniform particle size distribution, good dispersity and easily dispersed, good scratch resistance property, high hardness, excellent compatibility, it is suitable for reinforcement of polymers, it is recommended for TPO, polypropylene automotive exterior parts, bumpers and dashboard products and materials of grey or dark color auto.

 

Uncompacted form  

Loose bulk density :                           M.I. 93003                                     0.30 g/cm3 

Moisture content at 105 °C :             ISO 787/2 - M.I. 93005                0.2%

 

Brightness by Minolta CR300 

Y                                                            80.0

L*   (CIE)                                              83.0

a*   (CIE)                                              0.2

b*   (CIE)                                              0.5

 

Particle Size Distribution by Sedigraph                                                  by Laser Mastersizer 

Sedimentation analysis ,                                                                             Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                        Mie Theory  (ISO 13320-1)

Median Diameter -D50: 3.8 (4)*µm  D95: 7µm                                        Median Diameter - D50: 7 (10)*µm   D95: 16µm

Particle Size Distribution.png

 

Physical Properties  

Density                                             DIN 53193                       2.8 g/cm3

Specific Surface B.E.T.                 DIN 66131/2                     6 m2/g

Hardness                                        Mohs scale                       1

 

Chemical Analyses  

SiO2                                                                               60.5%

MgO                                                                                31.5%

CaO                                                                                0.2%

Fe2O3                                                                            0.2%

Al2O3                                                                             0.2%

Loss on Ignition at 1050°C                                       7.0%