Product Data Sheet                                                  H Series superfine(Compaction type)

This product is a highly pure white talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, high whiteness, good dispersity, excellent abrasion resistance and scratch resistance, easy to feed, good thermal stability and able to reduce the amount of other additives, it is suitable for reinforcement of modified plastics, it is recommended for polypropylene automotive exterior parts, interior parts, bumpers and dashboard products of high-end auto. Due to the compacted form, higher compounding throughput that can be achieved, it can be used as a nucleant in semi-crystalline polymers.

Compacted form  

Compacted bulk density :             M.I. 93003                                          0.55 g/cm3

Loose bulk density :                      M.I. 93003                                           0.11 g/cm3

Moisture content at 105 °C :         ISO 787/2 - M.I. 93005                     0.2%

Brightness by Minolta CR300 

Y                                                            96.0

L*   (CIE)                                              98.5

a*   (CIE)                                              0.2

b*   (CIE)                                              0.5

Particle Size Distribution by Sedigraph                                                    by Laser Mastersizer 

Sedimentation analysis ,                                                                               Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                         Mie Theory  (ISO 13320-1)

Median Diameter-D50:0.75(1.0)*µm D95: 2.5µm                                    Median Diameter-D50:3.5(5)*µm D95: 7.0µm

Physical Properties  

Density                                            DIN 53193                                   2.8 g/cm3

Specific Surface B.E.T.                 DIN 66131/2                               11 m2/g

Hardness                                        Mohs scale                                 1

Chemical Analyses  

SiO2                                                         61.5%

MgO                                                          31.5%

CaO                                                          0.2%

Fe2O3                                                      0.2%

Al2O3                                                       0.2%

Loss on Ignition at 1050°C                 6.0%