China Supplier of High Quality liaoning talc powder for rubber HYT-05C

日期:2013/9/17 17:55:15 人气:4241

Product Data Sheet                                                   HYT-05 C

This product is a special material of PC+ABS alloy material. Due to its high lamellarity, extreme fineness, uniform particle size distribution, high whiteness, good dispersity, excellent abrasion resistance and scratch resistance,easy to feed, good thermal stability and able to reduce the amount of other additives, it is suitable for filling and modification of alloy material and reinforcement of other polymers. Due to the compacted form, higher compounding throughput that can be achieved, it can be used as a nucleant in semi-crystalline polymers.

 

Compacted form  

Compacted bulk density :           M.I. 93003                                  0.45 g/cm3

Loose bulk density :                     M.I. 93003                                  0.11 g/cm3

Moisture content at 105 °C :       ISO 787/2 - M.I. 93005             0.2%

 

Brightness by Minolta CR300 

Y                                                                    96.0

L*   (CIE)                                                      98.5

a*   (CIE)                                                       0.2

b*   (CIE)                                                       0.5

 

Particle Size Distribution by Sedigraph                                                 by Laser Mastersizer 

Sedimentation analysis ,                                                                            Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                        Mie Theory  (ISO 13320-1)

Median Diameter-D50:0.75(1.0)*µmD95:2.5µm                                     Median Diameter-D50:3.5(5)*µm D95: 7.0µm

 

Particle Size Distribution.png

 Physical Properties  

Density                                                  DIN 53193                              2.8 g/cm3

Specific Surface B.E.T.                      DIN 66131/2                           11 m2/g

Hardness                                             Mohs scale                              1

Chemical Analyses  

SiO2                                                           61.0%

MgO                                                           31.5%

CaO                                                           0.2%

Fe2O3                                                        0.2%

Al2O3                                                         0.2%

Loss on Ignition at 1050°C                   6.5%