Chinese Supplier of quality Talc powder for papermaking 8000 meshes

日期:2013/9/17 17:56:32 人气:4710

Product Data Sheet                                       8000 meshes

 

This product is a highly pure white talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, good dispersity, more platy, excellent improved stiffness/impact balance of products, unique performance, low shrinkage rate, excellent scratch resistance property, it is suitable for reinforcement of high-end polymers and nucleant in semi-crystalline polymers, it is recommended for EPDM+ PP, PBT, PET, PLA products and related biodegradable plastics.

 

Uncompacted form  

Loose bulk density :                         M.I. 93003                                     0.11 g/cm3

Moisture content at 105 °C :           ISO 787/2 - M.I. 93005                0.2%

 

Brightness by Minolta CR300 

Y                                             96.0

L*   (CIE)                               98.5

a*   (CIE)                                0.2

b*   (CIE)                                0.5

 

Particle Size Distribution by Sedigraph                                                   by Laser Mastersizer 

Sedimentation analysis ,                                                                              Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                         Mie Theory  (ISO 13320-1)

Median Diameter -D50: 0.75 (1.0)*µm  D95: 2.5µm                               Median Diameter - D50: 3.5 (5)*µm   D95: 7.0µm

Particle Size Distribution.png

 

Physical Properties  

Density                                         DIN 53193                            2.8 g/cm3

Specific Surface B.E.T.              DIN 66131/2                        11 m2/g

Hardness                                     Mohs scale                           1

 

Chemical Analyses  

SiO2                                                               60.5%

MgO                                                               31.5%

CaO                                                               0.2%

Fe2O3                                                           0.2%

Al2O3                                                            0.2%

Loss on Ignition at 1050°C                      7.0%