Wholesale transparent talc powder,talc powder for paint use,talc powder for papermaking Z Series 1500 meshes(Transparent Grade)

日期:2016/9/14 10:20:01 人气:2925

Product data sheet                                                 Z Series 1500 meshes(Transparent Grade)

This product is a highly pure transparent talc. Due to its uniform particle size distribution, good dispersity, high whiteness, easily dispersed, good scratch resistance property, high hardness, excellent compatibility, high transparency and excellent transparency, it is suitable for reinforcement of polymers, it is recommended for filling of transparent polymers, especially for filling of masterbatch of thin film.

 

Uncompacted form  

Loose bulk density :                         M.I. 93003                                      0.20 g/cm3

Moisture content at 105 °C :           ISO 787/2 - M.I. 93005                 0.2%

 

Brightness by Minolta CR300 

Y                                                  96.0

L*   (CIE)                                    98.5

a*   (CIE)                                    0.2

b*   (CIE)                                    0.5

  

Particle Size Distribution by Sedigraph                                                  by Laser Mastersizer 

Sedimentation analysis ,                                                                             Laser diffraction ,

Stokes’ Law  (ISO 13317-3)                                                                        Mie Theory  (ISO 13320-1)

Median Diameter -D50: 3.0 (3)*µm  D95: 6.5µm                                    Median Diameter - D50: 5.8 (6)*µm   D95: 14.0µm

Particle Size Distribution.png

 

Physical Properties  

Density                                              DIN 53193                              2.8 g/cm3

Specific Surface B.E.T.                  DIN 66131/2                           6 m2/g

Hardness                                         Mohs scale                             1

 

Chemical Analyses  

SiO2                                                                      55.5%

MgO                                                                       31.5%

CaO                                                                       0.2%

Fe2O3                                                                   0.2%

Al2O3                                                                    0.2%

Loss on Ignition at 1050°C                              9.0%